Kimya TPU-92A filament
Kimya TPU-92A 3D Filament
The TPU-92A 3D Filament makes printing flexible parts and solvent resistant.
- FLEXIBILITY
- RESISTANCE TO ABRASION
- CHEMICAL RESISTANCE
- ELASTICITY
PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 245°C
PLATFORM TEMPERATURE : 85°C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.159 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@210°C – 2,16 kg) | 16.5 g/10min |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 33 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 210°C |
| Bed T° | 85°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 37/2/500 | 90 MPa |
| Tensile Strength | ISO 37/2/500 | 43.1 MPa | |
| Tensile strain at strength | ISO 37/2/500 | 350 % | |
| Tensile Stress at Break | ISO 37/2/500 | 41.7 MPa | |
| Tensile strain at break | ISO 37/2/500 | 351.6 % | |
| Flexural modulus | ISO 178 | 81 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 3 MPa | |
| Flexural strain at flexural strength | ISO 178 | >5 % | |
| Charpy impact resistance | ISO 179-1/1eA | No Break | |
| Shore Hardness | ISO 868 | 92A |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |