Kimya PLA-HI 750g filament

Kimya PLA-HI 750g filament

Kimya

Regular price $44.95 $46.00 Sale


Kimya PLA-HI 750g filament

 

Kimya PLA-HI 3D Filament

The 3D PLA-HI filament has been formulated to quadruple its impact resistance compared to PLA-S.

  • EASY TO PRINT
  • RESISTANCE TO IMPACT
  • NO ODOR
  • BIOSOURCED MATTER

 

PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 200°C
PLATFORM TEMPERATURE : 60°C

 

Made in USA. Ship from USA.

 

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.21 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@210°C – 2,16 kg) 5.7 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-220°C) 60 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-220°C) 156 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 50 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 200°C
Bed T° 60°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,491 MPa
Tensile Strength ISO 527-2/5A/50 43 MPa
Tensile strain at strength ISO 527-2/5A/50 2 %
Tensile Stress at Break ISO 527-2/5A/50 22.9 MPa
Tensile strain at break ISO 527-2/5A/50 4.2 %
Flexural modulus ISO 178 2,097 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 62.8 MPa
Charpy impact resistance ISO 179-1/1eA 16.5 kJ/m²
Shore Hardness ISO 868 76,8D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.