Kimya PETG Carbon black filament

Kimya PETG Carbon black filament

Kimya

Regular price $61.20 $61.20 Sale


Kimya PETG Carbon black filament

 

Kimya PETG Carbon 3D Filament

PETG CARBON has an excellent tensile modulus. PETG is reinforced with carbon fibers.

  • NO DELAMINATION
  • HIGH RIGIDITY
  • REINFORCMENT
  • POST-PRINTING PROCESSES POSSIBLE

 

PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 225°C
PLATFORM TEMPERATURE : 60°C

 

Diameter : 1.75mm
Net Weight : 500g
Color : Black

 

Made in USA. Ship from USA.

 

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.317 g/cm3
Moisture rate INS-6711 < 10 %
Melt flow index (MFI) ISO 1133-1 (@225°C – 2.16 kg) 9.7 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-300°C) 76 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 60 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 225°C
Bed T° 60°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 4,015 MPa
Tensile Strength ISO 527-2/5A/50 52.9 MPa
Tensile strain at strength ISO 527-2/5A/50 2.4 %
Tensile Stress at Break ISO 527-2/5A/50 41.3 MPa
Tensile strain at break ISO 527-2/5A/50 3.4 %
Flexural modulus ISO 178 2,987 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 80.4 MPa
Flexural strain at flexural strength ISO 178 4 %
Charpy impact resistance ISO 179-1/1eA 4.03 kJ/m²
Shore Hardness ISO 868 76,4D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.