Kimya HIPS-R 3D Filament
The HIPS-R 3D filament has many features:
- Impact resistance
- 100% made from recycled material
Warranty ARMOR 2 years.
Diameter : 1.75mm
Net Weight : 500g
Color : light grey
OUR TIPS FOR BETTER PRINTING
PRINT SPEED: 50mm / s
T ° PRINT: 250 ° C
T ° TRAY: 90 ° C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm |
| Density | ISO 1183-1 | 1.03 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@200°C – 5 kg) | 4.7 - 7.1 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-260°C) | 97 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 50 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 250°C |
| Bed T° | 95°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,273 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 23.7 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 1.5 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 16.7 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 11.5 % | |
| Flexural modulus | ISO 178 | 1,533 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 36.2 MPa | |
| Shore Hardness | ISO 868 | 76,6D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |