Kimya ABS Kevlar 3D Filament
ABS KEVLAR has been deisgned for 3D printing by a precise formulation of aramid fibers into ABS materials.
- NO SHRINKAGE
- LOW WARPING
- SMOOTH SURFACE
- LIGHT WEIGHT OBJECTS
Diameter : 1.75mm
Net Weight : 500g
Color : Black
PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 260°C
PLATFORM TEMPERATURE : 100°C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.037 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Melt flow index (MFI) | ISO 1133-1 (@220°C – 10 kg) | 14.8 g/10min |
Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 100 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 50 mm/s |
Infill | 100% - rectilinear |
Infill Angle | 45°/-45° |
Nozzle Temperature | 260°C |
Bed T° | 100°C |
PRINTED SPECIMENS PROPERTIES
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,775 MPa |
Tensile Strength | ISO 527-2/5A/50 | 31.1 MPa | |
Tensile strain at strength | ISO 527-2/1A/50 | 2.3 % | |
Tensile Stress at Break | ISO 527-2/5A/50 | 27.7 MPa | |
Tensile strain at break | ISO 527-2/5A/50 | 4.9 % | |
Flexural modulus | ISO 178 | 1,509 MPa | |
Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 44.7 MPa | |
Shore Hardness | ISO 868 | 65,2D |