Kimya ABS Carbon 3D Filament

Kimya ABS Carbon 3D Filament

Kimya

Regular price $60.60 $58.00 Sale


Kimya ABS Carbon 3D Filament

ABS CARBON FILAMENT improves interlayer adhesion and increases compression strength.

  • NO SHRINKAGE
  • BETTER TENSILE MODULUS THAN ABS
  • BETTER INTERLAYER ADHESION
  • LIGHT WEIGHT OBJECTS

Diameter : 1.75mm / 2.85mm

Net Weight : 500g

Color : Black

 

PRINT SETTINGS:

  • PRINT SPEED : 50 mm/s
  • EXTRUSION TEMPERATURE : 260°C
  • PLATFORM TEMPERATURE : 100°

 

Made in USA. Ship from USA.

 

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.032 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@220°C – 10 kg) 35.7 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-220°C) 100 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-220°C) 30 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 50 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 260°C
Bed T° 100°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,189 MPa
Tensile Strength ISO 527-2/5A/50 37.4 MPa
Tensile Stress at Break ISO 527-2/5A/50 33.2 MPa
Tensile strain at break ISO 527 3.1 %
Flexural modulus ISO 178 1,822 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 56.6 MPa
Flexural strain at flexural strength ISO 178 >5 %
Charpy impact resistance ISO 179-1/1eA 7.3 kJ/m²
Shore Hardness ISO 868 93D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.