Kimya TPU-R 1.75mm 750g translucent filament
Kimya TPU-R 3D Filament
The TPU-R 3D filament has many features:
- Flexible
- 100% made from recycled materials
Diameter : 1.75mm
Net Weight : 500g
Color : Translucent
OUR TIPS FOR BETTER PRINTING
PRINT SPEED: 33mm / s
T ° PRINT: 210 ° C
T ° TRAY: 85 ° C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm |
| Density | ISO 1183-1 | 1.14 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@200°C – 5 kg) | 42 - 45 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 90-190°C) | -33 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 33 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 210°C |
| Bed T° | 85°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 37/2/500 | 55.2 MPa |
| Tensile Strength | ISO 37/2/500 | 27.7 MPa | |
| Tensile strain at strength | ISO 37/2/500 | >300 % | |
| Tensile Stress at Break | ISO 37/2/500 | 27.4 MPa | |
| Tensile strain at break | ISO 37/2/500 | >300 % | |
| Flexural modulus | ISO 178 | 45.6 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 1.9 MPa | |
| Charpy impact resistance | ISO 180 | No Break | |
| Shore Hardness | ISO 868 | 90A |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |