Kimya PETG-S filament
Kimya PETG-S 3D Filament
The PETG-S Kimya 3D Filament offers the perfect balance of flexibility and strength.
- No smell
- High flexibility
- Resistance to impact
- Food contact compliant
- Hydrophobe
PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 225°C
PLATFORM TEMPERATURE : 60°C
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.274 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@225°C – 2.16 kg) | 12.1 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 80 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 50 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 225°C |
| Bed T° | 60°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,833 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 46.6 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 3.3 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 11.1 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 24.3 % | |
| Flexural modulus | ISO 178 | 1,641 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 57.5 MPa | |
| Flexural strain at flexural strength | ISO 178 | 5 % | |
| Charpy impact resistance | ISO 179-1/1eA | 4.0 kJ/m² | |
| Shore Hardness | ISO 868 | 72.5D |