Kimya PETG Carbon black filament
Kimya PETG Carbon 3D Filament
PETG CARBON has an excellent tensile modulus. PETG is reinforced with carbon fibers.
- NO DELAMINATION
- HIGH RIGIDITY
- REINFORCMENT
- POST-PRINTING PROCESSES POSSIBLE
PRINT SETTINGS:
PRINT SPEED : 50 mm/s
EXTRUSION TEMPERATURE : 225°C
PLATFORM TEMPERATURE : 60°C
Diameter : 1.75mm
Net Weight : 500g
Color : Black
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.317 g/cm3 |
| Moisture rate | INS-6711 | < 10 % |
| Melt flow index (MFI) | ISO 1133-1 (@225°C – 2.16 kg) | 9.7 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 76 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 60 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 225°C |
| Bed T° | 60°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 4,015 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 52.9 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 2.4 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 41.3 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 3.4 % | |
| Flexural modulus | ISO 178 | 2,987 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 80.4 MPa | |
| Flexural strain at flexural strength | ISO 178 | 4 % | |
| Charpy impact resistance | ISO 179-1/1eA | 4.03 kJ/m² | |
| Shore Hardness | ISO 868 | 76,4D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |