Kimya PEKK Carbon 500g grey
Kimya PEKK Carbon 3D Filament
PEKK CARBON FILAMENT is easier to print than PEI or PEEK. It is designed for highly technical applications.
- HEAT RESISTANCE
- ABRASION RESISTANCE
- CHEMICAL RESISTANCE
- FLAME RETARDANT UL94 V0
Diameter : 1.75mm
Net Weight : 500g
Color : Grey
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.27 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-410°C) | 160 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 20-40 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 370-380°C |
| Bed T° | 150°C |
| Chamber T° | 80°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| THERMAL PROPERTIES | Maximum use T° | - | 150 °C |
| ELECTRICAL PROPERTIES | Dielectric constant | IEC 60243-1 (100µm) | 84 KV/mm |
| Surface resistivity | ASTM D257 | 1016 Ohms/m² | |
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527 | 2,900 MPa |
| Tensile Strength | ISO 527 | 39.1 MPa | |
| Tensile strain at break | ISO 527 | 3.2 % | |
| Flexural modulus | ISO 178 | 2,924 MPa |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |