Kimya PEKK-A 3D Filament
The PEKK-A filament made from Arkema’s KEPSTAN® is intended for technical applications requiring high resistance to temperature (up to 150 ° C).
- HEAT RESISTANCE
- ABRASION RESISTANCE
- CHEMICAL RESISTANCE
- FLAME RETARDANT – UL94 V0
Kimya’s 2-year warranty.
Diameter : 1.75mm / 2.85 mm
Net Weight : 250g / 500g
Color : Amber
RINT SETTINGS:
PRINT SPEED : 20-40 mm/s
EXTRUSION TEMPERATURE : 360-400°C
PLATFORM TEMPERATURE : 110-170°C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.261 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@380°C – 5 kg) | 37 - 47 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-410°C) | 159 °C |
| Heat distortion temperature (HDT) (1.8 MPa) | ISO 75f | |
| Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min – 20-410°C) | 308 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 20-40 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 370-380°C |
| Bed T° | 110-125°C |
| Chamber T° | 60-80°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| THERMAL PROPERTIES | Maximum use T° | - | 150 °C |
| Thermal conductivity | ASTM E1530-11 | 0.21 W/mK | |
| ELECTRICAL PROPERTIES | Dielectric constant | IEC 60243-1 (100µm) | 84 KV/mm |
| Surface resistivity | ASTM D257 | 1016 Ohms/m² | |
| OUTGASSING | Total Mass Loss (TML) | ASTM E 595 | 0.27 % |
| Collected Volatile Condensable Material (CVCM) | ASTM E 595 | 0 0.01 % | |
| Water Vapor Recovered (WVR) | ASTM E 595 | 0.29 % | |
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 2,510 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 65 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 5 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 48 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | >5 % | |
| Flexural modulus | ISO 178 | 1,660 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 63.2 MPa | |
| Flexural strain at flexural strength | ISO 178 | >5 % | |
| Charpy impact resistance | ISO 179-1/1eA | 2.5 kJ/m² |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |