Kimya ABS-S 3D Black 2.2kg Filament
The ABS-S 3D filament has many features:
- Temperature resistance
- Impact resistance
Warranty ARMOR 2 years.
Diameter : 1.75mm
Net Weight : 2.2kg
Color : black
OUR TIPS FOR BETTER PRINTING
PRINT SPEED: 25-30mm / s
T ° PRINT: 260 ° C
T ° TRAY: 85-95 ° C
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.035 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@220°C – 10 kg) | 3.5 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 107 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 25-50 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 260°C |
| Bed T° | 85-95°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,484 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 35.3 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 2.7 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 22.8 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 9.8 % | |
| Flexural modulus | ISO 178 | 1,443 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 43.6 MPa | |
| Flexural strain at flexural strength | ISO 178 | 5 % | |
| Shore Hardness | ISO 868 | 70D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |