Kimya ABS Carbon 3D Filament
ABS CARBON FILAMENT improves interlayer adhesion and increases compression strength.
- NO SHRINKAGE
- BETTER TENSILE MODULUS THAN ABS
- BETTER INTERLAYER ADHESION
- LIGHT WEIGHT OBJECTS
Diameter : 1.75mm / 2.85mm
Net Weight : 500g
Color : Black
PRINT SETTINGS:
- PRINT SPEED : 50 mm/s
- EXTRUSION TEMPERATURE : 260°C
- PLATFORM TEMPERATURE : 100°
Made in USA. Ship from USA.
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.032 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@220°C – 10 kg) | 35.7 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 100 °C |
| Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min – 20-220°C) | 30 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 50 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 260°C |
| Bed T° | 100°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 2,189 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 37.4 MPa | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 33.2 MPa | |
| Tensile strain at break | ISO 527 | 3.1 % | |
| Flexural modulus | ISO 178 | 1,822 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 56.6 MPa | |
| Flexural strain at flexural strength | ISO 178 | >5 % | |
| Charpy impact resistance | ISO 179-1/1eA | 7.3 kJ/m² | |
| Shore Hardness | ISO 868 | 93D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |